Customized Static Control Anti Static Agents Chemicals High Efficiency For Industrial Use
製品詳細
| プロセスメソッド: | プラスチック内部添加剤 | パフォーマンス機能: | 低表面抵抗コンパウンド |
|---|---|---|---|
| 加工の優位性: | 簡単なカラーマッチング 帯電防止 | ||
| ハイライト |
Customized Anti Static Agents Chemicals,Static Control Anti Static Agents Chemicals,Industrial Use Anti Static Agents |
||
製品説明
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength at 25℃ | MPa | GB/T 528 | 12.2 |
| Elongation at Break at 25℃ | % | GB/T 528 | 788 |
| Shore Hardness, 3s | HD | GB/T 2411 | 46.5 |
| Density | g/cm³ | GB/T 533 | 1.222 |
| Melt Flow Rate (210℃, 2.16kg) | g/10min | GB-3682 | 10.62 |
| Surface Resistance | Ω | GB/T 1410 | 1.6*10⁶ |
- Blend ASTPEEN permanent polymeric antistatic agent with the base resin thoroughly by dry mixing
- Add dispersants, fillers, pigments, etc., to the mixture as required
- Melt and compound using a twin-screw extruder to process into masterbatch
- Special masterbatch available (can be directly used in production after uniform dry mixing with raw materials at ratio of 1:1, 1:2 or 1:3)
- Any conventional processing methods can be applied: open mixing/internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming, etc.
- A suitable compatibiliser may be added as required
- Before processing, pre-drying of the mixture is recommended (suggested conditions: drying at 85-125℃ for 2-4 hours) to prevent performance loss
- Use up the product as soon as possible after opening
- Any unused product must be stored in a sealed container to prevent moisture absorption
- Bulk products with vacuum bag leakage and residual materials must be dried at 85-125℃ for 2-4 hours before use
- Moisture absorption may result in degraded performance during processing
製品のハイライト
Permanent Antistatic Agent for Polymers ASTPEEN 600 White/pale yellow elastomer particles featuring low surface resistance and easy color matching. Surface resistance ≤10⁶ Ω, hardness ~95A, melting point ~200°C. Recommended Applications Recommended for modification of HIPS, ABS, TPEE, PC, PBT, PP ...
25D Thermoplastic Polyurethane Elastomer Granule TPEE Plascic Raw Material
Thermoplastic Polyurethane Elastomer TPEE 25D Product Overview TPEE 25D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to maintain optimal material properties. Technical Specifications Test Items Test Method 25D Tensile Strength, 25℃, MPa GB/T 528 5.5 Elongation at Break, 25℃, % GB/T 528 410 Shore Hardness, 3s, HD GB/T 2411 25 Density, g/cm³ GB/T 533 1
Industrial Grade Thermoplastic Polyurethane TPU Elastomer Granule 72D Shore Hardness
Thermoplastic Polyurethane Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre
50D Hardness Thermoplastic Polyurethane Elastomer Industrial Use Automotive Grade
Thermoplastic Polyurethane Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing
Thixotropic Water Stop Paste Waterblocking Compound For Optical Cables
Waterblocking Compound For Optical Fiber Cable Water blocking grease for optical and electrical cables is a thixotropic paste-form chemical water-blocking material specially designed for optical cables, communication cables and power cables. It is compounded through an advanced process. Its core function is to expand rapidly upon contact with water when the outer sheath of a cable is damaged and water intrudes, forming a gel-like barrier that effectively prevents further