Industrial Thermoplastic Polyurethane Elastomer TPEE 63D Hardness Impact Resistance
Product Details
| Core Category: | Thermoplastic Polyester Elastomer (TPEE) | Technical Specification: | 63D Shore Hardness TPEE |
|---|---|---|---|
| Performance Feature: | High Impact Resistance Polymer | Processing Advantage: | Easy Processing TPEE Resin |
| Highlight |
Industrial Thermoplastic Polyurethane Elastomer,63D Hardness Thermoplastic Polyurethane Elastomer |
||
Product Description
| Test Items | Test Method | 63D |
|---|---|---|
| Tensile Strength, 25℃, MPa | GB/T 528 | 32.3 |
| Elongation at Break, 25℃, % | GB/T 528 | 599 |
| Shore Hardness, 3s, HD | GB/T 2411 | 63 |
| Density, g/cm³ | GB/T 533 | 1.246 |
| Melt Flow Rate, g/10min (230℃, 2.16kg) | GB-3682 | 29.34 |
When the temperature exceeds the melting point, moisture in the resin will cause hydrolysis, resulting in degraded physical properties and increased brittleness. Generally, hydrolysis will not occur when the moisture content is below 0.1%. Therefore, materials exposed to air must be re-dried before use.
Recommended drying conditions: 80℃ for 3-4 hours, or 60℃ overnight.
TPEE exhibits excellent processability and can be easily formed into various products via plastic processing methods such as injection molding, extrusion, and blow molding. The recommended processing temperature for this product ranges from 180℃ to 260℃, with the specific temperature depending on the process and grade.
TPEE is hygroscopic and must be stored in a cool, dry place in sealed packaging. Any unused material after opening should be tightly resealed. Drying prior to processing is a critical step to ensure finished product quality; insufficient or no drying will result in a significant decline in the mechanical properties of the product.
- Rail Transit: Used in under-rail pads for light rail, high-speed rail, subway, and heavy-haul railway. Features appropriate dynamic-static ratio and excellent resilience.
- Automotive Components: Engine intake pipes, drive shaft boots, airbag housings, automotive fuel vapor hoses, fuel tanks, air brake hoses. Offers outstanding chemical resistance and weatherability for superior performance and longer service life.
- Electrical & Electronic: Fiber-optic cables, communication wiring equipment, antennas. Exhibits excellent heat resistance, elasticity, creep resistance and electrical insulation.
- Industrial Products: Hydraulic hoses, inflation tubes, gears, manipulators, couplings, seals, gaskets, shock absorbers.
Product Highlights
Thermoplastic Polyester Elastomer TPEE 63D Technical Specifications Test Items Test Method 63D Tensile Strength, 25℃, MPa GB/T 528 32.3 Elongation at Break, 25℃, % GB/T 528 599 Shore Hardness, 3s, HD GB/T 2411 63 Density, g/cm³ GB/T 533 1.246 Melt Flow Rate, g/10min (230℃, 2.16kg) GB-3682 29.34 ...
High Elasticity TPU Elastomer TPEE Material 45D Shore Hardness Abrasion Resistance
Thermoplastic Polyurethane Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the
40D Thermoplastic Polyurethane Elastomer TPU Pellets For Electronic Industry
Thermoplastic Polyurethane Elastomer TPEE 40D Product Overview TPEE 40D offers high impact resistance, stable performance, and easy processing capabilities, making it an ideal material for demanding industrial applications. Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during manufacturing operations. Critical Note: When temperature exceeds the melting point, moisture in the resin causes hydrolysis, resulting in degraded
55D Thermoplastic Polyurethane Elastomer TPEE Granules for Automotive Components
Thermoplastic Polyurethane Elastomer TPEE 55D Material Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during manufacturing operations. When the temperature exceeds the melting point, moisture in the resin will cause hydrolysis, resulting in degraded physical properties and increased brittleness. Generally, hydrolysis will not occur when the moisture content is below 0.1%. Therefore, materials exposed to air must be re-dried
UL94 V0 Grade TPEE Thermoplastic Polyester Elastomer High Elasticity For Electronics
TPEE Flame Retardant Material 70D Our TPEE Flame Retardant Material is a professionally modified special material independently developed by our company, characterized by low toxicity, environmental protection, and high-efficiency flame retardancy, stably reaching UL94 V0 grade. We provide flexible options of halogen-free and halogen-containing formulas to meet different environmental protection and usage requirements of global customers. The product combines excellent
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.