Partikel Agen Antistatik Tahan Panas Food Grade Untuk Produk Polimer
Detail Produk
| metode proses: | Aditif Plastik Internal | Fitur kinerja: | Aditif Ketahanan Permukaan Rendah |
|---|---|---|---|
| Properti Fisik: | Polimer Antistatis Berwarna | ||
| Menyoroti |
Partikel Agen Antistatik Permanen,Agen Antistatik Food Grade,Agen Antistatik Untuk Produk Polimer |
||
Deskripsi Produk
Kekerasan:95A
Titik leleh:~ 180°C
Penampilan:Partikel elastomer tembus pandang kuning pucat
| Titik pengujian | Satuan | Metode pengujian | Nilai Uji |
|---|---|---|---|
| Kekuatan tarik pada 25°C | MPa | GB/T 528 | 6.8 |
| Elongasi pada titik istirahat pada suhu 25°C | % | GB/T 528 | 100 |
| Kekerasan Pantai, 3s | HD | GB/T 2411 | 35 |
| Kepadatan | g/cm3 | GB/T 533 | 1.188 |
| Tingkat Aliran Peleburan (190°C, 2,16kg) | g/10menit | GB-3682 | 6.45 |
| Resistensi Permukaan | Oh | GB/T 1410 | 1.7*106 |
- Campurkan ASTPEEN agen antistatik polimer permanen dengan resin dasar secara menyeluruh dengan pencampuran kering
- Tambahkan dispersant, pengisi, pigmen, dll ke campuran sesuai kebutuhan
- Peleburan dan senyawa menggunakan ekstruder berkerut ganda untuk memproses menjadi masterbatch
- Masterbatch khusus tersedia (bisa digunakan langsung dalam produksi setelah pencampuran kering seragam dengan bahan baku pada 1:1, rasio 1:2 atau 1:3)
- Berlaku pada metode pengolahan konvensional: pencampuran terbuka/pencampuran internal, ekstrusi, cetakan injeksi, cetakan bertiup, ekstrusi film cor, busa
- Kompatibiliser yang cocok dapat ditambahkan sesuai kebutuhan (mencari produk tertentu)
- Rekomendasi pra pengeringan sebelum pengolahan: 85-125°C selama 2-4 jam untuk mencegah penurunan kinerja
- Gunakan produk sesegera mungkin setelah dibuka
- Simpan produk yang belum digunakan dalam wadah tertutup untuk mencegah penyerapan kelembaban
- Produk grosir dengan kebocoran kantong vakum dan bahan residu harus dikeringkan pada 85-125°C selama 2-4 jam sebelum digunakan
- Penyerapan kelembaban dapat mengakibatkan penurunan kinerja selama pengolahan
Pengolahan Keamanan:Perlengkapan pelindung umum (sarung tangan, masker debu) dianjurkan selama penanganan.
Bantuan Pertama:Jika terjadi kontak tidak sengaja dengan mata atau kulit, segera bilas dengan banyak air.
Sorotan Produk
ASTPEEN 310 Agen Antistatik Permanen untuk Polimer Partikel elastomer tembus pandang kuning pucat yang dirancang untuk kontrol statis yang efektif dalam aplikasi polimer. Spesifikasi Utama Resistensi permukaan:≤ 1*106 Ω Kekerasan:95A Titik leleh:~ 180°C Penampilan:Partikel elastomer tembus pandang ...
Granul TPEE Elastomer Poliester Termoplastik Kelas Industri Kekerasan Shore 72D
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
Elastisitas Tinggi Polyester Termoplastik Elastomer TPEE Material 45D Kekerasan Pantai Ketahanan Abrasi
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
Granul TPEE Fleksibilitas Tinggi Elastomer Poliester Termoplastik Bahan Baku TPEE 35D
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
Elastomer Poliester Termoplastik Kekerasan 50D Penggunaan Industri Tingkat Otomotif
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement