Food Grade Heat Resistance Antistatic Agent Particles For Polymers Products
Product Details
| Process Method: | Internal Plastic Additive | Performance Feature: | Low Surface Resistance Additive |
|---|---|---|---|
| Physical Property: | Colourable Antistatic Polymer | ||
| Highlight |
Permanent Anti static Agent Particles,Food Grade Antistatic Agent,Antistatic Agent For Polymers Products |
||
Product Description
Hardness: 95A
Melting Point: ~180℃
Appearance: Pale yellow translucent elastomer particles
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength at 25℃ | MPa | GB/T 528 | 6.8 |
| Elongation at Break at 25℃ | % | GB/T 528 | 100 |
| Shore Hardness, 3s | HD | GB/T 2411 | 35 |
| Density | g/cm³ | GB/T 533 | 1.188 |
| Melt Flow Rate (190℃, 2.16kg) | g/10min | GB-3682 | 6.45 |
| Surface Resistance | Ω | GB/T 1410 | 1.7*10⁶ |
- Blend ASTPEEN permanent polymeric antistatic agent with base resin thoroughly by dry mixing
- Add dispersants, fillers, pigments, etc., to mixture as required
- Melt and compound using twin-screw extruder to process into masterbatch
- Special masterbatch available (can be directly used in production after uniform dry mixing with raw materials at 1:1, 1:2 or 1:3 ratio)
- Applicable to conventional processing methods: open mixing/internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming
- Suitable compatibiliser may be added as required (consult for specific products)
- Pre-drying recommended before processing: 85-125℃ for 2-4 hours to prevent performance loss
- Use product as soon as possible after opening
- Store unused product in sealed container to prevent moisture absorption
- Bulk products with vacuum bag leakage and residual materials must be dried at 85-125℃ for 2-4 hours before use
- Moisture absorption may result in degraded performance during processing
Safety Handling: Non-toxic granular solid. General protective equipment (gloves, dust masks) recommended during handling.
First Aid: In case of accidental contact with eyes or skin, rinse immediately with plenty of water. Seek medical attention promptly if discomfort occurs.
Product Highlights
ASTPEEN 310 Permanent Antistatic Agent for Polymers Pale yellow translucent elastomer particles designed for effective static control in polymer applications. Features low surface resistance and easy color matching capabilities. Key Specifications Surface Resistance: ≤ 1*10⁶ Ω Hardness: 95A Melting ...
Industrial Grade Thermoplastic Polyester Elastomer Granule TPEE 72D Shore Hardness
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
High Elasticity Thermoplastic Polyester Elastomer TPEE Material 45D Shore Hardness Abrasion Resistance
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
High Flexibility TPEE Granule Thermoplastic Polyester Elastomer 35D TPEE Raw Material
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
50D Hardness Thermoplastic Polyester Elastomer Industrial Use Automotive Grade
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.