Pelet Elastomer Antifouling Agen Antistatik Permanen Tingkat Industri Polimer
Detail Produk
| Warna: | Putih/Kuning Pucat | metode proses: | Aditif Antistatis Internal |
|---|---|---|---|
| Fitur kinerja: | Aditif Polimer Disipatif Statis | Properti Fisik: | Antistatik Hitam Non-karbon |
| Menyoroti |
Agen Antistatik Antifouling,Agen antistatik kelas industri,Agen Antistatik Permanen dalam Polimer |
||
Deskripsi Produk
| Item Uji | Unit | Metode Uji | Nilai Uji |
|---|---|---|---|
| Kekuatan Tarik pada 25℃ | MPa | GB/T 528 | 61.8 |
| Perpanjangan Putus pada 25℃ | % | GB/T 528 | 768 |
| Kekerasan Shore, 3s | HD | GB/T 2411 | 62.5 |
| Kepadatan | g/cm³ | GB/T 533 | 1.163 |
| Laju Alir Leleh (220℃, 2.16kg) | g/10min | GB-3682 | 15.4 |
| Resistansi Permukaan | Ω | GB/T 1410 | 2.4*10⁷ |
- Campurkan agen antistatik polimer permanen ASTPEEN dengan resin dasar secara menyeluruh dengan pencampuran kering
- Tambahkan pendispersi, pengisi, pigmen, dll., ke dalam campuran sesuai kebutuhan
- Lelehkan dan campurkan menggunakan ekstruder sekrup ganda untuk diproses menjadi masterbatch
- Masterbatch khusus tersedia (dapat langsung digunakan dalam produksi setelah pencampuran kering yang merata dengan bahan baku pada rasio 1:1, 1:2 atau 1:3)
- Kompatibel dengan metode pemrosesan konvensional: pencampuran terbuka/pencampuran internal, ekstrusi, cetakan injeksi, cetakan tiup, ekstrusi film cor, pembusaan
- Pendukung kompatibilitas yang sesuai dapat ditambahkan sesuai kebutuhan
- Pengeringan awal direkomendasikan sebelum pemrosesan (85-125℃ selama 2-4 jam) untuk mencegah hilangnya kinerja
- Gunakan produk sesegera mungkin setelah dibuka
- Simpan produk yang tidak terpakai dalam wadah tertutup untuk mencegah penyerapan kelembaban
- Produk curah dengan kebocoran kantong vakum dan sisa bahan harus dikeringkan pada 85-125℃ selama 2-4 jam sebelum digunakan
- Penyerapan kelembaban dapat menyebabkan penurunan kinerja selama pemrosesan
- Semua bahan baku adalah senyawa polimer dengan proses produksi ramah lingkungan
- Tidak ada gas buang, air limbah, atau residu industri yang dihasilkan
- Padatan granular tidak beracun - peralatan pelindung umum direkomendasikan (sarung tangan, masker debu)
- Jika terjadi kontak yang tidak disengaja dengan mata atau kulit, segera bilas dengan banyak air
- Segera cari pertolongan medis jika terjadi ketidaknyamanan
Sorotan Produk
Agen Antistatik Permanen untuk Polimer - ASTPEEN 301 Pelet elastomer transparan putih/kuning pucat dengan resistansi permukaan rendah dan pencocokan warna yang mudah. Resistansi permukaan ≤ 10⁷ Ω, kekerasan 63D, titik leleh 190℃. Aplikasi Produk Direkomendasikan untuk produk tahan panas termasuk PA, ...
Granul TPEE Elastomer Poliester Termoplastik Kelas Industri Kekerasan Shore 72D
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
Elastisitas Tinggi Polyester Termoplastik Elastomer TPEE Material 45D Kekerasan Pantai Ketahanan Abrasi
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
Granul TPEE Fleksibilitas Tinggi Elastomer Poliester Termoplastik Bahan Baku TPEE 35D
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
Elastomer Poliester Termoplastik Kekerasan 50D Penggunaan Industri Tingkat Otomotif
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement
Silakan gunakan formulir kontak pertanyaan online kami di bawah ini jika Anda memiliki pertanyaan, tim kami akan menghubungi Anda sesegera mungkin.