Antifouling Elastomer Pellets Permanent Antistatic Agent In Polymer Industrial Grade
Product Details
| Color: | White/pale Yellow | Process Method: | Internal Antistatic Additive |
|---|---|---|---|
| Performance Feature: | Static Dissipative Polymer Additive | Physical Property: | Non-carbon Black Antistatic |
| Highlight |
Antifouling Antistatic Agent,Industrial Grade Antistatic Agent,Permanent Antistatic Agent In Polymer |
||
Product Description
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength at 25℃ | MPa | GB/T 528 | 61.8 |
| Elongation at Break at 25℃ | % | GB/T 528 | 768 |
| Shore Hardness, 3s | HD | GB/T 2411 | 62.5 |
| Density | g/cm³ | GB/T 533 | 1.163 |
| Melt Flow Rate (220℃, 2.16kg) | g/10min | GB-3682 | 15.4 |
| Surface Resistance | Ω | GB/T 1410 | 2.4*10⁷ |
- Blend ASTPEEN permanent polymeric antistatic agent with the base resin thoroughly by dry mixing
- Add dispersants, fillers, pigments, etc., to the mixture as required
- Melt and compound using a twin-screw extruder to process into masterbatch
- Special masterbatch available (can be directly used in production after uniform dry mixing with raw materials at ratio of 1:1, 1:2 or 1:3)
- Compatible with conventional processing methods: open mixing/internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming
- Suitable compatibiliser may be added as required
- Pre-drying recommended before processing (85-125℃ for 2-4 hours) to prevent performance loss
- Use product as soon as possible after opening
- Store unused product in sealed container to prevent moisture absorption
- Bulk products with vacuum bag leakage and residual materials must be dried at 85-125℃ for 2-4 hours before use
- Moisture absorption may result in degraded performance during processing
- All raw materials are polymeric compounds with eco-friendly production process
- No waste gas, waste water or industrial residue generated
- Non-toxic granular solid - general protective equipment recommended (gloves, dust masks)
- In case of accidental contact with eyes or skin, rinse immediately with plenty of water
- Seek medical attention promptly if discomfort occurs
Product Highlights
Permanent Antistatic Agent for Polymers - ASTPEEN 301 White/pale yellow translucent elastomer pellets featuring low surface resistance and easy color matching. Surface resistance ≤ 10⁷ Ω, hardness 63D, melting point 190℃. Product Applications Recommended for heat-resistant products including PA, PC, ...
Industrial Grade Thermoplastic Polyester Elastomer Granule TPEE 72D Shore Hardness
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
High Elasticity Thermoplastic Polyester Elastomer TPEE Material 45D Shore Hardness Abrasion Resistance
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
High Flexibility TPEE Granule Thermoplastic Polyester Elastomer 35D TPEE Raw Material
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
50D Hardness Thermoplastic Polyester Elastomer Industrial Use Automotive Grade
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.