Permanent Antistatic Agent Granules Static Control In Plastic And Electronic Material
Product Details
| Product Color: | White/pale Yellow | Process Method: | Internal Plastic Additive |
|---|---|---|---|
| Performance Feature: | Low Resistance Static Dissipative | Physical Property: | Non-carbon Black Antistatic |
| Highlight |
Static Control Permanent Antistatic Agent,Antistatic Agent for Electronic Material,Permanent Antistatic Agent Granules |
||
Product Description
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength at 25℃ | MPa | GB/T 528 | 10.8 |
| Elongation at Break at 25℃ | % | GB/T 528 | 261 |
| Shore Hardness, 3s | HD | GB/T 2411 | 44.5 |
| Density | g/cm³ | GB/T 533 | 1.260 |
| Melt Flow Rate (210℃, 2.16kg) | g/10min | GB-3682 | 33.96 |
| Surface Resistance | Ω | GB/T 1410 | 5.7*10⁶ |
- Blend ASTPEEN permanent polymeric antistatic agent with the base resin thoroughly by dry mixing
- Add dispersants, fillers, pigments, etc., to the mixture as required
- Melt and compound using a twin-screw extruder to process into masterbatch
- Special masterbatch available (can be directly used in production after uniform dry mixing with raw materials at ratio of 1:1, 1:2 or 1:3)
- Compatible with conventional processing methods: open mixing/internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming
- Suitable compatibiliser may be added as required
- Pre-drying recommended before processing (85-125℃ for 2-4 hours) to prevent performance loss
- Use product as soon as possible after opening and store unused product in sealed container to prevent moisture absorption
Product Highlights
ASTPEEN 200 Permanent Antistatic Agent for Polymers ASTPEEN 200 is a white/pale yellow elastic granule featuring low surface resistance and easy color matching. This permanent polymeric antistatic agent offers surface resistance ≤ 10⁶ Ω, hardness 45D, and melting range 85°C. Product Specifications ...
Industrial Grade Thermoplastic Polyester Elastomer Granule TPEE 72D Shore Hardness
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
High Elasticity Thermoplastic Polyester Elastomer TPEE Material 45D Shore Hardness Abrasion Resistance
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
High Flexibility TPEE Granule Thermoplastic Polyester Elastomer 35D TPEE Raw Material
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
50D Hardness Thermoplastic Polyester Elastomer Industrial Use Automotive Grade
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement