Partikel Elastomer Transparan Agen Antistatik Permanen untuk Industri Elektronik
Detail Produk
| metode proses: | Aditif Polimer Internal | Fitur kinerja: | Disipatif Statis Efisiensi Tinggi |
|---|---|---|---|
| Properti Fisik: | Masterbatch Antistatis Berwarna | Nama Produk: | Agen Antistatis Permanen |
| Jenis: | agen antistatis | ||
| Menyoroti |
Agen Antistatik Polimer Permanen,Partikel Elastomer Agen Antistatik,Agen Antistatik untuk Industri Elektronik |
||
Deskripsi Produk
| Titik pengujian | Satuan | Metode pengujian | Nilai Uji |
|---|---|---|---|
| Kekuatan tarik pada 25°C | MPa | GB/T 528 | 8.0 |
| Elongasi pada titik istirahat pada suhu 25°C | % | GB/T 528 | 1079 |
| Kekerasan Pantai, 3s | HD | GB/T 2411 | 25 |
| Kepadatan | g/cm3 | GB/T 533 | 1.065 |
| Tingkat Aliran Peleburan (190°C, 2,16kg) | g/10menit | GB- 3682 | 26.4 |
| Resistensi Permukaan | Oh | GB/T 1410 | 1.1*107 |
- Campurkan agen antistatik polimer permanen ASTPEEN dengan resin dasar secara menyeluruh dengan cara mencampur kering.
- Tambahkan dispersant, pengisi, pigmen, dll, ke dalam campuran sesuai kebutuhan, kemudian lebur dan campuran menggunakan ekstruder dua sekrup untuk memproses menjadi masterbatch.
- Setiap metode pengolahan konvensional dapat diterapkan, seperti pencampuran terbuka / pencampuran internal, ekstrusi, cetakan injeksi, cetakan hembusan, ekstrusi film cor, busa, dll.
- Kompatibiliser yang sesuai dapat ditambahkan sesuai kebutuhan (silakan hubungi kami untuk produk tertentu).
- Sebelum pengolahan, direkomendasikan untuk mengeringkan campuran terlebih dahulu sesuai kebutuhan (kondisi yang disarankan: pengeringan pada 85-125 °C selama 2-4 jam) untuk mencegah kehilangan kinerja selama pengolahan.
- Gunakan produk sesegera mungkin setelah dibuka.
- Setiap produk yang tidak digunakan harus disimpan dalam wadah tertutup untuk mencegah penyerapan kelembaban.
- Produk massal dengan kebocoran kantong vakum yang disebabkan oleh transportasi atau transfer, serta bahan residu setelah pembukaan dan sampel tambahan, harus dikeringkan pada 85-125 °C selama 2-4 jam sebelum digunakan.
- Jika tidak, penyerapan kelembaban dari udara dapat mengakibatkan degradasi kinerja selama pengolahan berikutnya.
Sorotan Produk
Agen antistatik permanen untuk polimer ASTPEEN 300 Partikel elastomer tembus pandang putih/kuning muda dengan ketahanan permukaan rendah dan pencocokan warna yang mudah. Spesifikasi Produk Resistensi permukaan ≤ 1*106 Ω, kekerasan 80A, titik leleh 170°C. Aplikasi yang direkomendasikan Direkomendasik...
Granul TPEE Elastomer Poliester Termoplastik Kelas Industri Kekerasan Shore 72D
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
Elastisitas Tinggi Polyester Termoplastik Elastomer TPEE Material 45D Kekerasan Pantai Ketahanan Abrasi
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
Granul TPEE Fleksibilitas Tinggi Elastomer Poliester Termoplastik Bahan Baku TPEE 35D
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
Elastomer Poliester Termoplastik Kekerasan 50D Penggunaan Industri Tingkat Otomotif
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement
Silakan gunakan formulir kontak pertanyaan online kami di bawah ini jika Anda memiliki pertanyaan, tim kami akan menghubungi Anda sesegera mungkin.