Translucent Elastomer Particles Permanent Anti Static Agent For Electronics Industry
Product Details
| Process Method: | Internal Polymer Additive | Performance Feature: | High-Efficiency Static Dissipative |
|---|---|---|---|
| Physical Property: | Colorable Antistatic Masterbatch | Productname: | Permanent Antistatic Agent |
| Type: | Antistatic Agent | ||
| Highlight |
Permanent Polymer Antistatic Agent,Anti Static Agent Elastomer Particles,Anti Static Agent For Electronics Industry |
||
Product Description
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength at 25℃ | MPa | GB/T 528 | 8.0 |
| Elongation at Break at 25℃ | % | GB/T 528 | 1079 |
| Shore Hardness, 3s | HD | GB/T 2411 | 25 |
| Density | g/cm³ | GB/T 533 | 1.065 |
| Melt Flow Rate (190℃, 2.16kg) | g/10min | GB- 3682 | 26.4 |
| Surface Resistance | Ω | GB/T 1410 | 1.1*10⁷ |
- Blend ASTPEEN permanent polymeric antistatic agent with the base resin thoroughly by dry mixing.
- Add dispersants, fillers, pigments, etc., to the mixture as required, then melt and compound using a twin-screw extruder to process into masterbatch.
- Any conventional processing methods can be applied, such as open mixing / internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming, etc.
- A suitable compatibiliser may be added as required (please consult us for specific products).
- Before processing, pre-drying of the mixture is recommended as needed (suggested conditions: drying at 85-125℃ for 2-4 hours) to prevent performance loss during processing.
- Use up the product as soon as possible after opening.
- Any unused product must be stored in a sealed container to prevent moisture absorption.
- Bulk products with vacuum bag leakage caused by transportation or transfer, as well as residual materials after opening and complimentary samples, must be dried at 85-125℃ for 2-4 hours before use.
- Otherwise, moisture absorption from air may result in degraded performance during subsequent processing.
Product Highlights
Permanent Antistatic Agent for Polymers ASTPEEN 300 White/light yellow translucent elastomer particles featuring low surface resistance and easy color matching. Product Specifications Surface resistance ≤ 1*10⁶ Ω, hardness 80A, melting point 170℃. Recommended Applications Recommended for film ...
Industrial Grade Thermoplastic Polyester Elastomer Granule TPEE 72D Shore Hardness
Thermoplastic Polyester Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre-dried
High Elasticity Thermoplastic Polyester Elastomer TPEE Material 45D Shore Hardness Abrasion Resistance
Thermoplastic Polyester Elastomer TPEE 45D High impact resistance and stable performance, easy processing thermoplastic polyurethane elastomer. Technical Specifications Test Items Test Method 45D Tensile Strength, 25℃, MPa GB/T 528 16.2 Elongation at Break, 25℃, % GB/T 528 453 Shore Hardness, 3s, HD GB/T 2411 45 Density, g/cm³ GB/T 533 1.147 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 12.9 Processing Guidelines TPEE must be pre-dried prior to processing to ensure the resin
High Flexibility TPEE Granule Thermoplastic Polyester Elastomer 35D TPEE Raw Material
Thermoplastic Polyester Elastomer TPEE 35D Technical Specifications Test Items Test Method 35D Tensile Strength, 25℃, MPa GB/T 528 9.6 Elongation at Break, 25℃, % GB/T 528 450 Shore Hardness, 3s, HD GB/T 2411 35 Density, g/cm³ GB/T 533 1.138 Melt Flow Rate, g/10min (220℃, 2.16kg) GB-3682 21.04 Processing Requirements TPEE must be pre-dried prior to processing to ensure the resin remains dry during processing. When the temperature exceeds the melting point, moisture in the
50D Hardness Thermoplastic Polyester Elastomer Industrial Use Automotive Grade
Thermoplastic Polyester Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing Requirement
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.