Anti Moisture Permanent Anti Static Agent 1.207g/Cm3 For Electronic Components
تفاصيل المنتج
| نطاق التطبيق: | عامل الاستاتيكيه للبوليمرات | ميزة الأداء: | تبديد ثابت منخفض المقاومة |
|---|---|---|---|
| ميزة المعالجة: | مادة مضافة سهلة لمطابقة الألوان | ||
| إبراز |
Anti Moisture Permanent Anti Static Agent,Anti Static Agent for Electronic Components,Anti Static Agent for Electronic Components |
||
وصف المنتج
ASTPEEN 806 features low surface resistance and easy color matching. This white/pale yellow elastomer particle product offers surface resistance ≤10⁶ Ω, hardness 50D, and melting point ~200℃.
- Recommended for PC, ABS, PBT, PET, TPEE and other materials with high processing temperature and surface hardness requirements
- Suitable for extrusion (sheets, plates), injection molding, molding and other processes (pelletizing required)
- Widely used in plastic modification, industrial tools, electronics industry, cleanroom equipment and other fields
- Product Model: Type ASTPEEN 806
| Test Item | Unit | Test Method | Test Value |
|---|---|---|---|
| Tensile Strength (25℃) | MPa | GB/T 528 | 8.0 |
| Elongation at Break (25℃) | % | GB/T 528 | 415 |
| Shore Hardness (3s) | HD | GB/T 2411 | 31 |
| Density | g/cm³ | GB/T 533 | 1.207 |
| Melt Flow Rate (220℃, 2.16kg) | g/10min | GB/T 3682 | 0.24 |
| Melt Flow Rate (220℃, 5kg) | g/10min | GB/T 3682 | 1.78 |
| Surface Resistance | Ω | GB/T 1410 | 1.2×10⁶ |
It is generally recommended to add directly to the material at a ratio of 10-25%. The optimal dosage shall be determined experimentally based on the target surface resistivity and the type of material used.
- Blend ASTPEEN permanent polymeric antistatic agent with the base resin thoroughly by dry mixing
- Add dispersants, fillers, pigments, etc., to the mixture as required
- Melt and compound using a twin-screw extruder to process into masterbatch
- Special masterbatch available (can be directly used in production after uniform dry mixing with raw materials at ratio of 1:1, 1:2 or 1:3)
- Any conventional processing methods can be applied: open mixing/internal mixing, extrusion, injection moulding, blow moulding, cast film extrusion, foaming, etc.
- A suitable compatibiliser may be added as required (please consult us for specific products)
- Before processing, pre-drying of the mixture is recommended (suggested conditions: drying at 85-125℃ for 2-4 hours) to prevent performance loss
- Use up the product as soon as possible after opening
- Any unused product must be stored in a sealed container to prevent moisture absorption
- Bulk products with vacuum bag leakage caused by transportation or transfer, as well as residual materials after opening and complimentary samples, must be dried at 85-125℃ for 2-4 hours before use
- Otherwise, moisture absorption from air may result in degraded performance during subsequent processing
- Packaging: 25 kg per bag, paper-plastic composite bag or aluminium-plastic vacuum bag
- Storage: Store in a cool, dry and ventilated warehouse, away from direct sunlight, heat sources and ignition sources
- All raw materials are polymeric compounds with an eco-friendly production process and no waste gas, waste water or industrial residue
- This product is non-toxic granular solid
- General protective equipment (e.g. gloves, dust masks) is recommended during handling
- In case of accidental contact with eyes or skin, rinse immediately with plenty of water
- Seek medical attention promptly if discomfort occurs
أبرز المنتجات
Permanent Antistatic Agent for Polymers ASTPEEN 806 ASTPEEN 806 features low surface resistance and easy color matching. This white/pale yellow elastomer particle product offers surface resistance ≤10⁶ Ω, hardness 50D, and melting point ~200℃. Product Overview Recommended for PC, ABS, PBT, PET, TPEE ...
25D Thermoplastic Polyurethane Elastomer Granule TPEE Plascic Raw Material
Thermoplastic Polyurethane Elastomer TPEE 25D Product Overview TPEE 25D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to maintain optimal material properties. Technical Specifications Test Items Test Method 25D Tensile Strength, 25℃, MPa GB/T 528 5.5 Elongation at Break, 25℃, % GB/T 528 410 Shore Hardness, 3s, HD GB/T 2411 25 Density, g/cm³ GB/T 533 1
Industrial Grade Thermoplastic Polyurethane TPU Elastomer Granule 72D Shore Hardness
Thermoplastic Polyurethane Elastomer TPEE 72D Product Overview TPEE 72D offers high impact resistance, stable performance, and easy processing capabilities, making it ideal for demanding industrial applications. Technical Specifications Test Items Test Method 72D Tensile Strength, 25℃, MPa GB/T 528 38.5 Elongation at Break, 25℃, % GB/T 528 475 Shore Hardness, 3s, HD GB/T 2411 72 Density, g/cm³ GB/T 533 1.290 Processing Requirements Pre-drying is essential: TPEE must be pre
50D Hardness Thermoplastic Polyurethane Elastomer Industrial Use Automotive Grade
Thermoplastic Polyurethane Elastomer TPEE 50D TPEE 50D offers high impact resistance, stable performance, and easy processing capabilities. This thermoplastic polyurethane elastomer requires proper pre-drying before processing to ensure optimal performance. Technical Specifications Test Items TPEE 50D Shore Hardness, 3s, HD 51 Tensile Strength, 25℃, MPa 19.2 Elongation at Break, 25℃, % 587 Melt Flow Rate, g/10min (220℃, 2.16kg) 1.0/6.9 Density, g/cm³ 1.175 Processing
Thixotropic Water Stop Paste Waterblocking Compound For Optical Cables
Waterblocking Compound For Optical Fiber Cable Water blocking grease for optical and electrical cables is a thixotropic paste-form chemical water-blocking material specially designed for optical cables, communication cables and power cables. It is compounded through an advanced process. Its core function is to expand rapidly upon contact with water when the outer sheath of a cable is damaged and water intrudes, forming a gel-like barrier that effectively prevents further
يرجى استخدام نموذج الاتصال عبر الإنترنت في الأسفل إذا كان لديك أي أسئلة، وسوف يعود فريقنا إليك في أقرب وقت ممكن.